Enhanced oxygen diffusivity in interfaces of nanocrystalline ZrO2.Y2O3.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 12655074.
- Also identified by PMC identifier 153014.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
First measurements of oxygen grain boundary diffusion coefficients in nanocrystalline yttria-doped ZrO(2) (n-ZrO(2).6.9 mol % Y(2)O(3)) are presented. The (18)O diffusion profiles measured by secondary ion mass spectroscopy are much deeper in the nanocrystalline specimens than in single crystals. An oxygen diffusivity, D(B), in the grain boundaries can be deduced, which is approximately 3 orders of magnitude higher than in single crystals. From the present data the temperature variation of the oxygen grain boundary diffusivity, D(B) = 2.0 x 10(-5) exp (-0.91 eVk(B)T) m(2)s, and the oxygen surface exchange coefficient, k = 1.4 x 10(-2) exp (-1.13 eVk(B)T) ms, are derived.