Compressive strength, fluoride release and recharge of fluoride-releasing materials.

Abstract

The compressive strength, fluoride releases and recharge profiles of 15 commercial fluoride-releasing restorative materials have been studied. The materials include glass ionomers (Fuji IX, Ketac Molar, Ketac Silver, and Miracle Mix), resin-modified glass ionomers (Fuji II LC Improved, Photac-Fil, and Vitremer), compomers (Compoglass, Dyract AP, F2000, and Hytac) and composite resins (Ariston pHc, Solitaire, Surefil and Tetric Ceram). A negative linear correlation was found between the compressive strength and fluoride release (r(2)=0.7741), i.e., restorative materials with high fluoride release have lower mechanical properties. The fluoride-releasing ability can be partially regenerated or recharged by using a topical fluoride agent. In general, materials with higher initial fluoride release have higher recharge capability (r(2)=0.7088). Five equations have been used in curve fitting to describe the cumulative fluoride release from different materials. The equation [F](c)=[F](I)(1-e(-bt))+betat best describes the cumulative fluoride release for most glass ionomers, resin-modified glass ionomers, and some high fluoride-releasing compomers and composites, whereas [F](c)=[F](I)/(t(1/2)+t)+alphat best describes the cumulative fluoride release for most compomers and composite resins. The clinic applications of different fluoride-releasing materials have also been discussed.