Interaction of hydroxyapatite-titanium at elevated temperature in vacuum environment.

Abstract

In this study, the interaction between hydroxyapatite (HA) and titanium (Ti) at elevated temperature in vacuum environment was investigated. The 80 wt% HA-20 wt% Ti powder mixtures and 90 wt% HA-10 wt% Ti powder mixtures were dry pressed and heat-treated at 1100 degrees C in vacuum environment. HA powders and the commercially pure Ti powders were used as controls. The heat-treated samples were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy, scanning electron microscope (SEM) and energy disperse spectra. XRD and SEM indicated densification of metallic Ti specimens during the in-vacuum heat treatment. Heat treatment of HA specimens in vacuum resulted in the loss of hydroxyl groups as well the formation of a secondary beta-tricalcium phosphate phase. Metallic Ti was not observed in the in-vacuum heat-treated HA-Ti specimens. However, alpha-tricalcium phosphate, tetracalcium phosphate and calcium titanium oxide were observed for the in-vacuum heat-treated HA-Ti specimens. It was concluded that the in-vacuum heat-treatment process completely converted the metal-ceramics composites to ceramic composites.