Synthesis and cell affinity of functionalized poly(L-lactide-co-beta-malic acid) with high molecular weight.

Abstract

A novel functionalized biodegradable poly(L-lactide-co-beta-benzyl malolactonate) (p-PLMA) with high molecular weight was synthesized through ring-opening copolymerization. Three p-PLMA copolymers with different beta-benzyl malolactonate content were synthesized. The molecular weight (M(w)) and tensile strength of the copolymer with 4 mol% beta-benzyl malolactonate content were 179,800 and 19.0MPa respectively, the molecular weight (M(w)) and tensile strength of p-PLMA decreased with beta-benzyl malolactonate content increasing. The hydrophilicity of the de-protected product: poly(L-lactide-co-beta-malic acid) (d-PLMA) increased with malic acid content increasing. The results of 3T3 mice fibroblasts cultivated on d-PLMA films showed that the cell adhesion on d-PLMA was better than that of PLLA and the cell attached efficiency of d-PLMA with 8 mol% malic acid content was the highest. The cells grew well both on the surface and inside of d-PLMA scaffolds. The cell affinity of d-PLMA was better than that of PLLA.