High coercivity of ordered macroporous FePt films synthesized via colloidal templates.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 16178269.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
The preparation of a three-dimensionally (3D) ordered macroporous iron-platinum (FePt) film derived from monodisperse FePt nanoparticles (approximately 3 nm in diameter) and polystyrene latex particles (254 nm in diameter) is described. The prepared film has a hexagonally ordered porous structure and coercivity up to 10 kOe after annealing at a temperature of 600 degrees C. We also found that size of FePt particles was maintained at around 3 nm, even after annealing at a temperature of 600 degrees C.