Fracture of Ni-Ti superelastic alloy under sustained tensile load in physiological saline solution containing hydrogen peroxide.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 17311316.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
The fracture of Ni-Ti superelastic alloy has been investigated by a sustained tensile-loading test in physiological saline solution containing hydrogen peroxide (0.15M NaCl + 0.3M H(2)O(2)). The fracture always occurs when the applied stress exceeds the critical stress for martensite transformation. In contrast, under a low applied stress, the fracture does not always occur within 1000 h. The fracture is probably mainly caused by localized corrosion associated with the preferential dissolution of nickel ions. In 0.3M H(2)O(2) solution without NaCl, the fracture does not occur even under a high applied stress. The results of the present study imply that one reason for the fracture of the Ni-Ti superelastic alloy in vivo is localized corrosion due to the synergistic effects of hydrogen peroxide and sodium chloride under applied stress.
Medical subject headings
- Materials Testing
- Nickel
- Tensile Strength
- Titanium