Dynamic mechanical analysis and esterase degradation of dentin adhesives containing a branched methacrylate.

Abstract

A study of the dynamic mechanical properties and the enzymatic degradation of new dentin adhesives containing a multifunctional methacrylate are described. Adhesives contained 2-hydroxyethyl methacrylate, 2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy) phenyl]-propane, and a new multifunctional methacrylate with a branched side chain-trimethylolpropane mono allyl ether dimethacrylate (TMPEDMA). Adhesives were photopolymerized in the presence of 0, 8, and 16 wt % water to simulate wet bonding conditions in the mouth and compared with control adhesives. The degree of conversion as a function of irradiation time was comparable for experimental and control adhesives. In dynamic mechanical analysis, broad tan delta peaks were obtained for all samples, indicating that the polymerized networks are heterogeneous; comparison of the full-width-at-half-maximum values obtained from the tan delta curves indicated increased heterogeneity for samples cured in the presence of water and/or containing TMPEDMA. The experimental adhesive showed higher T(g) and higher rubbery modulus indicating increased crosslink density when compared with the control. The improvement in esterase resistance afforded by adhesives containing the TMPEDMA is greater when this material is photopolymerized in the presence of water, suggesting better performance in the moist environment of the mouth. The improved esterase resistance of the new adhesive could be explained in terms of the densely crosslinked network structure and/or the steric hindrance of branched alkyl side chains.