Microscopic origins for stabilizing room-temperature ferromagnetism in ultrathin manganite layers.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 20547875.
- Also identified by DOI 10.1073/pnas.1005693107 and PMC identifier 2900658.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
La(0.7)Sr(0.3)MnO(3) is a conducting ferromagnet at room temperature. Combined with thin SrTiO(3) layers, the resulting heterostructures could be used as highly spin-polarized magnetic-tunnel-junction memories. However, when shrunk to dimensions below an apparent critical thickness, the structures become insulating and ferromagnetic ordering is suppressed. Interface spin and charge modulations are thought to create an interfacial dead layer, thus fundamentally limiting the use of this material in atomic-scale devices. The thickness of this dead layer, and whether it is intrinsic, is still controversial. Here we use atomic-resolution electron spectroscopy to demonstrate that the degradation of the magnetic and transport properties of La(0.7)Sr(0.3)MnO(3)/SrTiO(3) multilayers correlates with atomic intermixing at the interfaces, and the presence of extended two-dimensional cation defects in the La(0.7)Sr(0.3)MnO(3) layers (in contrast to three-dimensional precipitates in thick films). When these extrinsic defects are eliminated, metallic ferromagnetism at room temperature can be stabilized in five-unit-cell-thick manganite layers in superlattices, placing the upper limit for any intrinsic dead layer at two unit cells per interface.