High-strength nanograined and translucent hydroxyapatite monoliths via continuous hydrothermal synthesis and optimized spark plasma sintering.

Abstract

The synthesis of high-strength, completely dense nanograined hydroxyapatite (bioceramic) monoliths is a challenge as high temperatures or long sintering times are often required. In this study, nanorods of hydroxyapatite (HA) and calcium-deficient HA (made using a novel continuous hydrothermal flow synthesis method) were consolidated using spark plasma sintering (SPS) up to full theoretical density in ∼5 min at temperatures up to 1000°C. After significant optimization of the SPS heating and loading cycles, fully dense HA discs were obtained which were translucent, suggesting very high densities. Significantly high three-point flexural strength values for such materials (up to 158 MPa) were measured. Freeze-fracturing of disks followed by scanning electron microscopy investigation revealed selected samples possessed sub-200 nm sized grains and no visible pores, suggesting they were fully dense.