Strong dependence of mechanical properties on fiber diameter for polymer-nanotube composite fibers: differentiating defect from orientation effects.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 20945879.
- Also identified by DOI 10.1021/nn102059c.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
We have prepared polyvinylalcohol-SWNT fibers with diameters from ∼1 to 15 μm by coagulation spinning. When normalized to nanotube volume fraction, V(f), both fiber modulus, Y, and strength, σ(B), scale strongly with fiber diameter, D: Y/V(f) ∝ D(-1.55) and σ(B)/V(f) ∝ D(-1.75). We show that much of this dependence is attributable to correlation between V(f) and D due to details of the spinning process: V(f) ∝ D(0.93). However, by carrying out Weibull failure analysis and measuring the orientation distribution of the nanotubes, we show that the rest of the diameter dependence is due to a combination of defect and orientation effects. For a given nanotube volume fraction, the fiber strength scales as σ(B) ∝ D(-0.29)D(-0.64), with the first and second terms representing the defect and orientation contributions, respectively. The orientation term is present and dominates for fibers of diameter between 4 and 50 μm. By preparing fibers with low diameter (1-2 μm), we have obtained mean mechanical properties as high as Y = 244 GPa and σ(B) = 2.9 GPa.