Static and dynamic moduli of posterior dental resin composites under compressive loading.

Abstract

Dental resin composites are commonly used as restorative materials for dental treatment. To comprehend the static and dynamic moduli of dental resin composites, we investigated the mechanical behaviors of resin composites under static and dynamic loading conditions. Four commercially available resin composites for posterior restorations were evaluated. The percentages, by weight, of inorganic fillers of resin composites were examined by the ashing technique. The static compressive tests were undertaken with a constant loading speed of 1.0 mm/min using a computer-controlled INSTRON testing machine. The dynamic properties of composites were determined using the split Hopkinson pressure bar (SHPB) technique. When inorganic filler content was increased, a remarkable increase in the static modulus and dynamic modulus were observed. Furthermore, there was a strong relationship between the static modulus and dynamic modulus (r(2) = 0.947). The SHPB technique clearly demonstrated the dynamic properties of composites, and was a useful technique for determining the mechanical behavior of composites under dynamic compressive loading.