Microstructural evolution of tin nanoparticles during in situ sodium insertion and extraction.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 23092238.
- Also identified by DOI 10.1021/nl303305c.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
The microstructural changes and phase transformations of tin nanoparticles during electrochemical sodiation were studied with a nanosized sodium ion battery using in situ transmission electron microscopy. It was found that the first sodiation process occurred in two steps; that is, the crystalline Sn nanoparticles were initially sodiated via a two-phase mechanism with a migrating phase boundary to form a Na-poor, amorphous Na(x)Sn alloy (x ~ 0.5), which was further sodiated to several Na-rich amorphous phases and finally to the crystallized Na(15)Sn(4) (x = 3.75) via a single-phase mechanism. The volumetric expansion was about 60% in the first step and 420% after the second step. However, despite the huge expansion, cracking or fracture was not observed, which is attributed to the second step of the single-phase sodiation that accommodates large portion of the sodiation-induced stress over the entire particle. Excellent cyclability was also observed during the reversible sodiation/desodiation cycles, showing great potential of Sn nanoparticles as a robust electrode material for rechargeable batteries.