Monodisperse antimony nanocrystals for high-rate Li-ion and Na-ion battery anodes: nano versus bulk.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 24484409.
- Also identified by DOI 10.1021/nl404165c.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
We report colloidal synthesis of antimony (Sb) nanocrystals with mean size tunable in the 10-20 nm range and with narrow size distributions of 7-11%. In comparison to microcrystalline Sb, 10 and 20 nm Sb nanocrystals exhibit enhanced rate-capability and higher cycling stability as anode materials in rechargeable Li-ion and Na-ion batteries. All three particle sizes of Sb possess high and similar Li-ion and Na-ion charge storage capacities of 580-640 mAh g(-1) at moderate charging/discharging current densities of 0.5-1C (1C-rate is 660 mA g(-1)). At all C-rates (0.5-20C, e.g. current densities of 0.33-13.2 Ag(1-)), capacities of 20 nm Sb particles are systematically better than for both 10 nm and bulk Sb. At 20C-rates, retention of charge storage capacities by 10 and 20 nm Sb nanocrystals can reach 78-85% of the low-rate value, indicating that rate capability of Sb nanostructures can be comparable to the best Li-ion intercalation anodes and is so far unprecedented for Na-ion storage.