Novel protein-repellent and biofilm-repellent orthodontic cement containing 2-methacryloyloxyethyl phosphorylcholine.

Abstract

The objectives of this study were to develop the first protein-repellent resin-modified glass ionomer cement (RMGI) by incorporating 2-methacryloyloxyethyl phosphorylcholine (MPC) for orthodontic applications, and to investigate the MPC effects on protein adsorption, biofilm growth, and enamel bond strength. MPC was incorporated into RMGI at 0% (control), 1.5%, 3%, and 5% by mass. Specimens were stored in water at 37°C for 1 and 30 days. Enamel shear bond strength (SBS) was measured, and the adhesive remnant index (ARI) scores were assessed. Protein adsorption onto the specimens was determined by a micro bicinchoninic acid method. A dental plaque microcosm biofilm model with human saliva as inoculum was used. The results showed that adding 3% of MPC into RMGI did not significantly reduce the SBS (p > 0.1). There was no significant loss in SBS for RMGI containing 3% MPC after water-aging for 30 days, as compared to 1 day (p > 0.1). RMGI with 3% MPC had protein adsorption that was 1/10 that of control. RMGI with 3% MPC greatly reduced the bacterial adhesion, and lactic acid production and colony-forming units of biofilms, while substantially increasing the medium solution pH containing biofilms. The protein-repellent and biofilm-repellent effects were not decreased after water-aging for 30 days. In conclusion, the MPC-containing RMGI is promising to reduce biofilms and white spot lesions without compromising orthodontic bracket-enamel bond strength. The novel protein-repellent method may have applicability to other orthodontic cements, dental composites, adhesives, sealants, and cements to repel proteins and biofilms. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 949-959, 2016.