Massive failure of TiNbN coating in surface engineered metal-on-metal hip arthroplasty: Retrieval analysis.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 25980456.
- Also identified by DOI 10.1002/jbm.b.33421.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
This article presents examination of a failed total hip replacement with surface engineered metal-on-metal (MoM) articulation. The implant was coated with a thin TiNbN film (Physical Vapor Deposition), and at retrieval 53 months after implantation the coating was abraded on weight-bearing part of the head and acetabular component. Scanning electron microscopy of bearing surfaces demonstrated multifocal crack formation, delamination of small film fragments, and formation of aggregates containing nanometer sized wear debris. We also observed coating damage in third body mechanism. Complex failure mechanism of TiNbN coating demonstrated in this study suggests insufficient bonding strength between the coating and substrate alloy and raise concerns regarding the use of such coatings in total hip arthroplasty with MoM bearing. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 1043-1049, 2016.
Medical subject headings
- Alloys
- Arthroplasty, Replacement, Hip
- Coated Materials, Biocompatible
- Hip Prosthesis
- Prosthesis Failure