Reconstruction of a quadriceps tendon tear using Polyvinylidene fluoride sutures and patellar screw fixation: A biomechanical study.

Abstract

Acute quadriceps tendon tears are infrequent injuries requiring surgical treatment. Improved stability after surgical repair may allow for earlier weight-bearing and range of motion. Therefore, a new implant was tested and compared with the "gold standard", using transosseous sutures. Quadriceps tendon tears were constructed using a cadaveric model of 12 fresh matched-pair specimens (aged 61-97; mean age: 82 years). The biomechanical testing compared non-absorbable suture anchors (Polyvinylidene fluoride) versus transosseous absorbable sutures (Polydioxanon). Following anatomic reconstruction, the repaired specimens were loaded until they failed (testing machine: Hounsfield H10KM, Redhill, United Kingdom; maximum force: 1000 N; load speed: 25 mm/min; maximum test length: 150 mm; pre-load: 5 N). Values for load until tear displacement, maximum load until complete failure of the construct (pullout or breakage of the sutures or anchors) and stiffness of the reconstruction were recorded. The stiffness found in the Polyvinylidene fluoride reconstruction (mean 9.83 N/mm) (standard deviation (SD) 7.75) showed a significant increase compared to the Polydioxanon reconstruction (mean 6.66 N/mm (SD 3.32); P=0.045). Transosseous fixation showed comparable results to the suture anchor system. There was no significant difference found in the maximum load to tear displacement (PVDF: 290.88 N (SD 106.01) vs. PDS: 266.75 N (SD 82.61); P=0.358). Using the Polyvinylidene fluoride thread showed comparable results to the established method in reconstruction of ruptured quadriceps tendon. Stiffness of the Polyvinylidene fluoride thread reconstruction was even greater than Polydioxanon thread. Improved stiffness may facilitate healing and is suggested as clinical relevance in reconstruction.