Stereoscopic Analysis of Silicone Breast Implant Shells Damaged by Surgical Instruments.

Abstract

Iatrogenic shell injury during the implantation and explantation of silicone gel breast implants may lead to eventual device failure. Identification of the patterns of injury caused by surgical instruments is important when attempting to characterize the cause of shell rupture. Understanding the true causes of device failure may help with its prevention. The purpose of this study was to microscopically characterize patterns of shell injury induced by various surgical instruments. Textured and smooth silicone gel implants were intentionally damaged with a variety of surgical instruments. Various scalpels and surgical scissors ranging in fineness were used to create full-thickness injuries in the implant shell. Optical microscopy and scanning electron microscopy were then used to image the injured area to determine patterns of injury. Full-thickness striations across the thickness of the shell could be seen with damage caused by scissors. The density of these striations correlated directly with the fineness of scissors used. No striations were seen with injuries caused by scalpels. Striations were only observed in injuries caused by scissors and suture needles. Striation density correlated with the coarseness of the cutting edge. No such striations were seen in shells damaged by a scalpel even when the angle of approach was changed. This difference can be of assistance in distinguishing between scissors versus scalpel injury of an implant shell.