Could larger diameter of 4th generation ceramic bearing decrease the rate of dislocation after THA?

Abstract

Fourth generation (Delta) ceramic bearing was developed to reduce dislocation after total hip arthroplasty (THA) by increasing the head diameter. We tested a hypothesis that 32/36 mm Delta ceramic bearing decreases the dislocation rate. We also evaluated ceramic-related complications and early outcome of this thin liner-on-large head ceramic bearing. We performed a prospective study on patients who underwent THA with use of 32/36 mm Delta ceramic bearing. The dislocation rate was compared with the historical dislocation rate of third generation 28 mm ceramic bearing. We also evaluated ceramic fracture, squeak, short-term results and survival. Follow-up period was minimum 2 years. Between April 2010 and February 2012, we enrolled 250 consecutive patients (278 hips). All patients received cementless prostheses. Four patients (4 hips) who received metal shells ≤ 46 mm and 28 mm heads were excluded. Three patients died and 2 patients were lost within 2 years. The remaining 241 patients (269 hips) were followed for 24-46 months. There were 142 men (161 hips) and 99 women (108 hips) with a mean age of 53.7 years (range, 17-75 years) at the index operation. Dislocation occurred in three hips (1.1%). An old age was a risk factor for dislocation. Ceramic fracture and squeaking did not occur in any patient. Mean Harris hip score was 90.3 points at the latest follow-up. All acetabular and femoral components had bone-ingrowth stability. No hip had detectable wear or osteolysis. The survival was 99.3% in the best case scenario and 97.8% in the worst at 48 months. Total hip arthroplasty with use of 32/36 mm Delta ceramic bearing showed lower incidence of hip dislocation compared with 28 mm third generation ceramic bearing. A caution should be paid to prevent a fall in senile patients even though a large head is used. The short-term results of THA with this type of ceramic articulation are encouraging and we did not find any ceramic-related complications.