Efficacy of fluoride varnishes for preventing enamel demineralization after interproximal enamel reduction. Qualitative and quantitative evaluation.

Abstract

To evaluate quantitatively and qualitatively the changes produced to enamel after interproximal reduction and subjected to demineralization cycles, after applying a fluoride varnish (Profluorid) and a fluoride varnish containing tricalcium phosphate modified by fumaric acid (Clinpro White). 138 interproximal dental surfaces were divided into six groups: 1) Intact enamel; 2) Intact enamel + demineralization cycles (DC); 3) Interproximal Reduction (IR); 4) IR + DC; 5) IR + Profluorid + DC; 6) IR + Clinpro White + DC. IR was performed with a 0.5 mm cylindrical diamond bur. The weight percentage of calcium (Ca), phosphorous (P) and fluoride (F) were quantified by energy-dispersive X-ray spectrometry (EDX). Samples were examined under scanning electron microscopy (SEM). The weight percentage of Ca was significantly higher (p<0.05) in Groups 1, 2 and 5 than Groups 4 and 6. No significant differences were detected in the weight percentage of Ca between Group 3 and the other groups (p>0.05). The weight percentage of P was similar among all six groups (p>0.05). F was detected on 65% of Group 6 surfaces. SEM images of Groups 4 and 6 showed signs of demineralization, while Group 5 did not. Profluorid application acts as a barrier against the demineralization of interproximally reduced enamel.