"Supertrap" at Work: Extremely Efficient Nonradiative Recombination Channels in MAPbI₃ Perovskites Revealed by Luminescence Super-Resolution Imaging and Spectroscopy.

Abstract

Organo-metal halide perovskites are some of the most promising materials for the new generation of low-cost photovoltaic and light-emitting devices. Their solution processability is a beneficial trait, although it leads to a spatial inhomogeneity of perovskite films with a variation of the trap state density at the nanoscale. Comprehending their properties using traditional spectroscopy therefore becomes difficult, calling for a combination with microscopy in order to see beyond the ensemble-averaged response. We studied photoluminescence (PL) blinking of micrometer-sized individual methylammonium lead iodide (MAPbI₃) perovskite polycrystals, as well as monocrystalline microrods up to 10 μm long. We correlated their PL dynamics with structure employing scanning electron and optical super-resolution microscopy. Combining super-resolution localization imaging and super-resolution optical fluctuation imaging (SOFI), we could detect and quantify preferential emitting regions in polycrystals exhibiting different types of blinking. We propose that blinking in MAPbI₃ occurs by the activation/passivation of a "supertrap" which presumably is a donor-acceptor pair able to trap both electrons and holes. As such, nonradiative recombination via supertraps, in spite being present at a rather low concentrations (10¹²-10¹⁵ cm^-3), is much more efficient than via all other defect states present in the material at higher concentrations (10¹⁶-10¹⁸ cm^-3). We speculate that activation/deactivation of a supertrap occurs by its temporary dissociation into free donor and acceptor impurities. We found that supertraps are most efficient in structurally homogeneous and large MAPbI₃ crystals where carrier diffusion is efficient, which may therefore pose limitations on the efficiency of perovskite-based devices.