Realizing Large-Area Arrays of Semiconducting Fullerene Nanostructures with Direct Laser Interference Patterning.

Abstract

We present a laser interference patterning method for the facile fabrication of large-area and high-contrast arrays of semiconducting fullerene nanostructures, which does not rely on a tedious application of sacrificial photoresists or photomasks. A solution-deposited phenyl-C₆₁-butyric acid methyl ester (PCBM) fullerene thin film is exposed to a spatially modulated illumination intensity, as realized by a two-beam laser interference. The PCBM molecules exposed to strong intensity are photochemically transformed into a low-solubility dimeric state, so that the nontransformed PCBM molecules can be selectively removed in a subsequent solution-based development step. Following brief exposure to green laser light (λ = 532 nm, t = 5 s, p = 0.17 W cm^-2) in the designed two-beam interference setup, and a 1 min development in a tuned acetone-chloroform solution, we realize well-defined and ordered PCBM nanostripe patterns with a fwhm line width of ∼200 nm and a repetition rate of ∼2.900 lines mm^-1 over a large area of 1 cm². We demonstrate that a desired high contrast is effectuated because the initial PCBM-dimer transformation rate is dependent on the square of the illumination intensity. The semiconducting functionality of the patterned fullerene is verified in a field-effect transistor experiment, where a typical PCBM nanostripe featured an electron mobility of 5.3 × 10^-3 cm² V^-1 s^-1 and an on/off ratio of 3 × 10³.