Formation of nanotubular TiO₂ structures with varied surface characteristics for biomaterial applications.

Abstract

Nanotubular structures were generated on the surface of titanium c.p. by anodization technique in an aqueous solution of acetic acid (14% v/v) with different sources of fluoride ion (HF, NaF, NH₄ F). The aim of using these three different compounds is to study the effect of the counterion (H⁺ , Na⁺ and NH4+) on the morphology, wettability and surface free energy of the modified surface. Nanotubes were generated at 10 and 15 V for each anodizing solution. To further improve surface characteristics, the samples were heat-treated at 600°C for 4 h and at 560°C for 3 h. SEM images revealed the formation of nanotubes in all anodizing conditions, while their diameter increased proportionally to the electric potential. X-ray diffraction and micro-Raman spectroscopy results showed the presence of both anatase and rutile phases, with a higher content of rutile in the coatings obtained using NH₄ F and an applied potential of 10 V. The heat-treatment significantly increased the wettability of the anodic coatings, especially for the coating obtained at 15 V with HF, which showed values < 7 degrees of contact angle. Besides, the nanotubes show a decrease in diameter due to the heat treatment, except for the nanotubes formed in NH₄ F. Depending on their surface properties (e.g. low contact angle and high surface free energy), these coatings potentially have great potential in biomedical applications, sensors devices, and catalytic applications among others. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 1341-1354, 2018.