Metastable Intermediates in Amorphous Titanium Oxide: A Hidden Role Leading to Ultra-Stable Photoanode Protection.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 30040905.
- Also identified by DOI 10.1021/acs.nanolett.8b02559.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Metastable intermediates represent a non-equilibrium state of matter that may impose profound impacts to materials properties beyond our understandings of monolithic and equilibrium systems. Here, we report a discovery of hidden metastable intermediates in amorphous TiO<sub>2</sub> thin films and their critical role in electrochemical damage. These intermediates have a non-bulk crystal-like structure and exhibit significantly higher electrical conductivity than both the amorphous and the crystalline phases. When these TiO<sub>2</sub> films are applied to protect Si photoelectrochemical (PEC) photoanodes, the intermediates can induce localized high electrical currents that largely accelerate the etching of the TiO<sub>2</sub> film and the Si electrode underneath. The intermediates can be effectively suppressed by raising their nucleation barrier via reducing the film thickness from 24 to 2.5 nm. The homogeneous amorphous TiO<sub>2</sub>-film-coated Si photoanodes achieved more than 500 h of PEC water oxidation at a steady photocurrent density of over 30 mA·cm<sup>-2</sup>.