Picosecond Charge Transfer and Long Carrier Diffusion Lengths in Colloidal Quantum Dot Solids.

Abstract

Quantum dots (QDs) are promising candidates for solution-processed thin-film optoelectronic devices. Both the diffusion length and the mobility of photoexcited charge carriers in QD solids are critical determinants of solar cell performance; yet various techniques offer diverse values of these key parameters even in notionally similar films. Here we report diffusion lengths and interdot charge transfer rates using a 3D donor/acceptor technique that directly monitors the rate at which photoexcitations reach small-bandgap dot inclusions having a known spacing within a larger-bandgap QD matrix. Instead of relying on photoluminescence (which can be weak in strongly coupled QD solids), we use ultrafast transient absorption spectroscopy, a method where sensitivity is undiminished by exciton dissociation. We measure record diffusion lengths of ∼300 nm in metal halide exchanged PbS QD solids that have led to power conversion efficiencies of 12%, and determine 8 ps interdot hopping of carriers following photoexcitation, among the fastest rates reported for PbS QD solids. We also find that QD solids composed of smaller QDs ( d = ∼3.2 nm) exhibit 5 times faster interdot charge transfer rates and 10 times lower trap state densities compared to larger ( d = ∼5.5 nm) QDs.