Fluoride-Induced Dynamic Surface Self-Reconstruction Produces Unexpectedly Efficient Oxygen-Evolution Catalyst.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 30517786.
- Also identified by DOI 10.1021/acs.nanolett.8b04466.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
The oxygen-evolution reaction (OER) is a key process in water-splitting systems, fuel cells, and metal-air batteries, but the development of highly active and robust OER catalyst by simple methods is a great challenge. Here, we report an in situ dynamic surface self-reconstruction that can dramatically improve the catalytic activity of electrocatalysts. A fluoride (F<sup>-</sup>)-incorporating NiFe hydroxide (NiFe-OH-F) nanosheet array was initially grown on Ni foam by a one-step hydrothermal method, which requires a 243 mV over-potential (η) to achieve a 10 mA cm<sup>-2</sup> current density with a Tafel slope of 42.9 mV dec<sup>-1</sup> in alkaline media. After the surface self-reconstruction induced by fluoride leaching under OER conditions, the surface of NiFe-OH-F was converted into highly mesoporous and amorphous NiFe oxide hierarchical structure, and the OER activity at η = 220 mV increases over 58-fold. The corresponding η at 10 mA cm<sup>-2</sup> decreases to 176 mV with an extreme low Tafel slope of 22.6 mV dec<sup>-1</sup>; this performance is superior to that of the state-of-the-art OER electrocatalysts.