A prospective study comparing tendon-to-bone interface healing using an interposition bioresorbable scaffold with a vented anchor for primary rotator cuff repair in sheep.

Abstract

The purpose of this study was to evaluate the biomechanical and histologic properties of rotator cuff repairs using a vented anchor attached to a bioresorbable interpositional scaffold composed of aligned PLGA (poly(l-lactide-co-glycoside)) microfibers in an animal model compared to standard anchors in an ovine model. Fifty-six (n = 56) skeletally mature sheep were randomly assigned to a repair of an acute infraspinatus tendon detachment using a innovative anchor-PLGA scaffold device (Treatment) or a similar anchor without the scaffold (Control). Animals were humanely euthanized at 7 and 12 weeks post repair. Histologic and biomechanical properties of the repairs were evaluated and compared. The Treatment group had a significantly higher fibroblast count at 7 weeks compared to the Control group. The tendon bone repair distance, percentage perpendicular fibers, new bone formation at the tendon-bone interface, and collagen type III deposition was significantly greater for the Treatment group compared with the Control group at 12 weeks (P ≤ .05). A positive correlation was identified in the Treatment group between increased failure loads at 12 weeks and the following parameters: tendon-bone integration, new bone formation, and collagen type III. No statistically significant differences in biomechanical properties were identified between Treatment and Control Groups (P > .05). Use of a vented anchor attached to a bioresorbable interpositional scaffold composed of aligned PLGA microfibers improves the histologic properties of rotator cuff repairs in a sheep model. Improved histology was correlated with improved final construct strength at the 12-week time point.