Multiscale Buffering Engineering in Silicon-Carbon Anode for Ultrastable Li-Ion Storage.

Abstract

Silicon-carbon (Si-C) hybrids have been proven to be the most promising anodes for the next-generation lithium-ion batteries (LIBs) due to their superior theoretical capacity (∼4200 mAh g^-1). However, it is still a critical challenge to apply this material for commercial LIB anodes because of the large volume expansion of Si, unstable solid-state interphase (SEI) layers, and huge internal stresses upon lithiation/delithiation. Here, we propose an engineering concept of multiscale buffering, taking advantage of a nanosized Si-C nanowire architecture through fabricating specific microsized wool-ball frameworks to solve all the above-mentioned problems. These wool-ball-like frameworks, prepared at high yields, nearly matching industrial scales (they can be routinely produced at a rate of ∼300 g/h), are composed of Si/C nanowire building blocks. As anodes, the Si-C wool-ball frameworks show ultrastable Li⁺ storage (2000 mAh g^-1 for 1000 cycles), high initial Coulombic efficiency of ∼90%, and volumetric capacity of 1338 mAh cm^-3. <i>In situ</i> TEM proves that the multiscale buffering design enables a small volume variation, only ∼19.5%, reduces the inner stresses, and creates a very thin SEI. The perfect multiscale elastic buffering makes this material more stable compared to common Si nanoparticle-assembled counterpart electrodes.