Modulation of thermodynamic and kinetic inverted phase behavior of block copolymers by inorganic polyoxometalates.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 31432861.
- Also identified by DOI 10.1039/c9sm01041f.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
The Keggin polyoxometalates (POM) H<sub>3</sub>PW<sub>12</sub>O<sub>40</sub> (PW) electrostatically complexed with poly(styrene-block-2-vinyl pyridine) (PS-b-P2VP) in DMF, and ordered microphase separation occurred through solvent evaporation. The phase behaviors of PS-b-P2VP/PW in bulk were systematically investigated by using SAXS and TEM to discover the effect of POM content and molecular weight of the block copolymers. Computational simulation was also performed to reveal the same phase transition sequence as the experimental results. As the POM content increases, the PS-b-P2VP/PW complex with a low molecular weight changed from lamellar phase (LAM) to hexagonal cylindrical phase (HEX), and finally transited into spherical phase (SPH). Unexpectedly, PS-b-P2VP/PW complexes with a high molecular weight were inclined to form a kinetic-trapped intermediate phase (inverted HEX). The mechanism of formation of inverted phases was proposed based on simulation that asymmetric swelling in the concentrated DMF solution would result in the ultimate kinetic-trapped nanostructure in the bulk.