In Vitro Evidence for Cell-Accelerated Corrosion Within Modular Junctions of Total Hip Replacements.

Abstract

Corrosion at modular junctions of total hip replacement (THR) remains a major concern today. Multiple types of damage modes have been identified at modular junctions, correlated with different corrosion characteristics that may eventually lead to implant failure. Recently, within the head-taper region of the CoCrMo retrieval implants, cell-like features and trails of etching patterns were observed that could potentially be linked to the involvement of cells of the periprosthetic region. However, there is no experimental evidence to corroborate this phenomenon. Therefore, we aimed to study the potential role of periprosthetic cell types on corrosion of CoCrMo alloy under different culture conditions, including the presence of CoCrMo wear debris. Cells were incubated with and without CoCrMo wear debris (obtained from a hip simulator) with an average particle size of 119 ± 138 nm. Electrochemical impedance spectroscopy (EIS) was used to evaluate the corrosion tendency, corrosion rate, and corrosion kinetics using the media after 24 h of cell culture as the electrolyte. Results of the study showed that there was lower corrosion resistance (p < 0.02) and higher capacitance (p < 0.05) within cell media from macrophages challenged with particles when compared with the other media conditions studied. The potentiodynamic results were also in agreement with the EIS values, showing significantly higher corrosion tendency (low E_corr ) (p < 0.0001) and high I_corr (p < 0.05) in media from challenged macrophages compared with media with H₂ O₂ solution. Overall, the study provides in vitro experimental evidence for the possible role of macrophages in altering the chemical environment within the crevice and thereby accelerating corrosion of CoCrMo alloy. © 2019 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 38:393-404, 2020.