Enhanced elasticity in poly(acrylic acid) gels via synthesis in the presence of high concentrations of select salts.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 31475721.
- Also identified by DOI 10.1039/c9sm01101c.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Poly(acrylic acid) (PAA) gels synthesized via free-radical polymerization of acrylic acid, N,N'-methylenebisacrylamide and high molarities of salts in water exhibit properties markedly different from PAA gels synthesized without salt, even when the latter are incubated in high-molarity salt solutions after gelation. Particularly noteworthy is unusual mechanical behaviour that includes substantially increased elongation, increased modulus, and rapid recovery after strain. The greatest enhancement in viscoelastic behaviour is evident in 2 M LiCl and ZnCl<sub>2</sub> samples, with LiCl samples having a modulus of 39 kPa and reaching an extension ratio of 10 and a fracture stress of 135 kPa, and ZnCl<sub>2</sub> samples having a modulus of 43 kPa and reaching an extension ratio of 8.5 and a fracture stress of 175 kPa. This enhanced elasticity is thought to be brought about by a combination of coiled but only weakly-entangled PAA chains with phase-separated regions of salt acting as a plasticizer and modulating intermolecular interactions among AA units.