Massive Vacancy Concentration Yields Strong Room-Temperature Ferromagnetism in Two-Dimensional ZnO.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 31524409.
- Also identified by DOI 10.1021/acs.nanolett.9b02581.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Two-dimensional (2D) ZnO nanosheets with highly concentrated Zn vacancies (V<sub>Zn</sub>) of up to approximately 33% were synthesized by ionic layer epitaxy at the water-toluene interface. This high cation vacancy concentration is unprecedented for ZnO and may provide unique opportunities to realize exotic properties not attainable in the conventional bulk form. After annealing, the nanosheets showed characteristic magnetic hysteresis with saturation magnetization of 57.2 emu/g at 5 K and 50.9 emu/g at room temperature. This value is 1 order of magnitude higher than other ZnO nanostructures and comparable to the conventional ferrimagnetic Fe<sub>3</sub>O<sub>4</sub>. Density functional theory calculations, with the support of experimental results, suggest that a high concentration of V<sub>Zn</sub> (approximately one-third of the Zn sites) can form spontaneously during synthesis when stabilized by H ions, and the formation of V<sub>Zn</sub> could be further facilitated by the presence of grain boundaries. It is essential to remove the H for the nanosheets to show ferromagnetism. The mechanisms identified for the origin of the high magnetism in ZnO nanosheets presents an intriguing example of a kinetically stabilized, non-equilibrium, highly defective 2D nanomaterial with a significantly enhanced physical property.