High-surface-area corundum by mechanochemically induced phase transformation of boehmite.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 31649198.
- Also identified by DOI 10.1126/science.aaw9377.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
In its nanoparticulate form, corundum (α-Al<sub>2</sub>O<sub>3</sub>) could lead to several applications. However, its production into nanoparticles (NPs) is greatly hampered by the high activation energy barrier for its formation from cubic close-packed oxides and the sporadic nature of its nucleation. We report a simple synthesis of nanometer-sized α-Al<sub>2</sub>O<sub>3</sub> (particle diameter ~13 nm, surface areas ~140 m<sup>2</sup> g<sup>-1</sup>) by the mechanochemical dehydration of boehmite (γ-AlOOH) at room temperature. This transformation is accompanied by severe microstructural rearrangements and might involve the formation of rare mineral phases, diaspore and tohdite, as intermediates. Thermodynamic calculations indicate that this transformation is driven by the shift in stability from boehmite to α-Al<sub>2</sub>O<sub>3</sub> caused by milling impacts on the surface energy. Structural water in boehmite plays a crucial role in generating and stabilizing α-Al<sub>2</sub>O<sub>3</sub> NPs.