Controlled Growth and Thickness-Dependent Conduction-Type Transition of 2D Ferrimagnetic Cr₂ S₃ Semiconductors.

Abstract

2D magnetic materials have attracted intense attention as ideal platforms for constructing multifunctional electronic and spintronic devices. However, most of the reported 2D magnetic materials are mainly achieved by the mechanical exfoliation route. The direct synthesis of such materials is still rarely reported, especially toward thickness-controlled synthesis down to the 2D limit. Herein, the thickness-tunable synthesis of nanothick rhombohedral Cr₂ S₃ flakes (from ≈1.9 nm to tens of nanometers) on a chemically inert mica substrate via a facile chemical vapor deposition route is demonstrated. This is accomplished by an accurate control of the feeding rate of the Cr precursor and the growth temperature. Furthermore, it is revealed that the conduction behavior of the nanothick Cr₂ S₃ is variable with increasing thickness (from 2.6 to 4.8 nm and >7 nm) from p-type to ambipolar and then to n-type. Hereby, this work can shed light on the scalable synthesis, transport, and magnetic properties explorations of 2D magnetic materials.