Design and evaluation of nano-hydroxyapatite/poly(vinyl alcohol) hydrogels coated with poly(lactic-co-glycolic acid)/nano-hydroxyapatite/poly(vinyl alcohol) scaffolds for cartilage repair.

Abstract

Poly(vinyl alcohol) (PVA) hydrogels have been widely used in synthetic cartilage materials. However, limitations of PVA hydrogels such as poor biomechanics and limited cell ingrowth remain challenges in this field. This work aimed to design novel nano-hydroxyapatite (nano-HA)/poly(vinyl alcohol) (PVA) hydrogels coated with a poly(lactic-co-glycolic acid) (PLGA)/nano-HA/PVA scaffold to counter the limitations of PVA hydrogels. The core, comprising nano-HA/PVA hydrogel, had the primary role of bearing the mechanical load. The peripheral structure, composed of PLGA/nano-HA/PVA, was designed to favor interaction with surrounding cartilage. The double-layer HA/PVA hydrogel coated with PLGA/HA/PVA scaffold was successfully prepared using a two-step molding method, and the mechanical properties and biocompatibility were characterized. The mechanical properties of the novel PLGA/HA/PVA scaffold modified HA/PVA hydrogel were similar to those of native cartilage and showed greater sensitivity to compressive stress than to tensile stress. Rabbit chondrocytes were seeded in the composites to assess the biocompatibility and practicability in vitro. The results showed that the peripheral component comprising 30 wt% PLGA/5 wt% HA/15 wt% PVA was most conducive to rabbit chondrocyte adhesion and proliferation. The study indicated that the double-layer HA/PVA hydrogel coated with PLGA/HA/PVA scaffold has the potential for cartilage repair.