Formation of a C15 Laves Phase with a Giant Unit Cell in Salt-Doped A/B/AB Ternary Polymer Blends.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 32866375.
- Also identified by DOI 10.1021/acsnano.0c06071.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Salt-doped A/B/AB ternary polymer blends, wherein an AB copolymer acts as a surfactant to stabilize otherwise incompatible A and B homopolymers, display a wide range of nanostructured morphologies with significant tunability. Among these structures, a bicontinuous microemulsion (BμE) has been a notable target. Here, we report the surprising appearance of a robust C15 Laves phase, at compositions near where the BμE has recently been reported, in lithium bis(trifluoromethane) sulfonimide (LiTFSI)-doped low-molar-mass poly(ethylene oxide) (PEO)/polystyrene (PS)/symmetric PS-<i>b</i>-PEO block copolymer blends. The materials were analyzed by a combination of small-angle X-ray scattering (SAXS), <sup>1</sup>H NMR spectroscopy, and impedance spectroscopy. The C15 phase emerges at a high total homopolymer volume fraction ϕ<sub>H</sub> = 0.8 with a salt composition <i>r</i> = 0.06 (Li<sup>+</sup>/[EO]) and persists as a coexisting phase across a large area of the isothermal phase diagram with high PS homopolymer compositions. Notably, the structure exhibits a huge unit cell size, <i>a</i> = 121 nm, with an unusually high micelle core volume fraction (<i>f</i><sub>core</sub> = 0.41) and an unusually low fraction of amphiphile (20%). This unit cell dimension is at least 50% larger than any previously reported C15 phase in soft matter, despite the low molar masses used, unlocking the possibility of copolymer-based photonic crystals without compromising processability. The nanostructured phase evolution from lamellar to hexagonal to C15 along the EO60 isopleth (ϕ<sub>PEO,homo-LiTFSI</sub>/ϕ<sub>H</sub> = 0.6) is rationalized as a consequence of asymmetry in the homopolymer solubility limit for each block, which leads to exclusion of PS homopolymer from the PS-<i>b</i>-PEO brush prior to exclusion of the PEO homopolymer, driving increased interfacial curvature and favoring the emergence of the C15 Laves phase.