Hydrothermally grown TiO₂-nanorods on surface mechanical attrition treated Ti: Improved corrosion fatigue and osteogenesis.

Abstract

Current bioactive modifications of Ti-based materials for promoting osteogenesis often decrease corrosion fatigue strength (σ_cf) of the resultant implants, thereby shortening their service lifespan. To solve this issue and accelerate the osteogenesis process, in the present study, a TiO₂ nanorods (TNR)-arrayed coating was hydrothermally grown on optimal surface mechanical attrition treated (SMATed) titanium (S-Ti). The microstructure, bond integrity, residual stress distribution, and corrosion fatigue of TNR-coated S-Ti (TNR/S-Ti) and the response of macrophages and bone marrow-derived mesenchymal stem cells (BMSCs) to TNR/S-Ti were investigated and compared with those of mechanically polished Ti (P-Ti), S-Ti, and TNR-coated P-Ti (TNR/P-Ti). S-Ti showed a nanograined layer and an underlying grain-deformed region with residual compressive stress, which was sustained even when it was hydrothermally coated with TNR. TNR on S-Ti showed nanotopography, composition, and bond strength almost identical to those of P-Ti. While TNR/P-Ti showed a considerable decrease in σ_cf compared to P-Ti, TNR/S-Ti exhibited an improved σ_cf which was even higher than that of P-Ti. Biologically, TNR/S-Ti enhanced adhesion, differentiation, and mineralization of BMSCs, and it also promoted adhesion and M1-to-M2 transition of macrophages as compared to S-Ti and P-Ti. With rapid phenotype switch of macrophages, the level of proinflammatory cytokines decreased, while anti-inflammatory cytokines were upregulated. In co-culture conditions, the migration, differentiation, and mineralization of BMSCs were enhanced by increased level of secretion factors of macrophages on TNR/S-Ti. The modified structure accelerated bone apposition in rabbit femur and is expected to induce a favorable immune microenvironment to facilitate osseointegration earlier; it can also simultaneously improve corrosion fatigue resistance of Ti-based implants and thereby enhance their service life.