Effect of resin cement space on the fatigue behavior of bonded CAD/CAM leucite ceramic crowns.

Abstract

This study evaluated the influence of occlusal resin cement space on the fatigue performance of bonded-leucite crowns to a dentin-analogue material. Leucite anatomical crowns were adhesively cemented to dentin-like preparations having distinct occlusal cement space (50, 100 and 300 μm) (n = 18), and subjected to step-stress fatigue testing (150 N - 350 N; step-size: 25 N; 20,000 cycles/step; 20 Hz). Fatigue data (load and number of cycles for failure) were analyzed using Kaplan-Meier and Mantel-Cox (log-rank) tests (p <0.05). Fractographic analysis and occlusal internal space measurements were also performed. There was no significant difference for the distinct occlusal cement layer (50 μm: 289 N, 136,111 cycles; 100 μm: 285 N, 132,778 cycles; 300 μm: 246 N, 101,667 cycles). Occlusal internal space analysis showed a mean thickness of 120.4 (50 μm), 174.9 (100 μm) and 337.2 (300 μm). All failures were radial cracks originating at the ceramic-cement interface. Distinct occlusal cement spaces had no effect on the fatigue behavior of anatomical leucite crowns.