A biomechanical matched-pair comparison of two different locking plates for tibial diaphyseal comminuted fracture: carbon fiber-reinforced poly-ether-ether-ketone (CF-PEEK) versus titanium plates.

Abstract

Several methods have been proposed to reduce plate construct stiffness and promote secondary bone healing. In this study, we explored the stiffness and strength of the new carbon fiber-reinforced poly-ether-ether-ketone (CF 50) plate compared with the titanium alloy plate (Ti6Al4V). Titanium and CF-PEEK locking plates were tested in a tibial non-osteoporotic diaphyseal comminuted fracture model to determine construct stiffness in axial compression, torsion, and bending. Subsequently, constructs were loaded until construct failure to determine construct strength. Relative to the titanium locking plate, the stiffness of the CF-PEEK locking plate was 6.8% and 30.8% lower in 200 N and 700 N axial compression, respectively (P < 0.05), 64.9% lower in torsion (P < 0.05), and 48.9% lower in bending (P < 0.05). The strength of the CF-PEEK locking plate was only 2.6% lower under axial compression, 7.8% lower in torsion, and 4.8% lower in bending than the titanium locking plate (P > 0.05). The CF-PEEK locking plate significantly reduced axial, torsion, and bending stiffness compared with the titanium locking plate. Nonetheless, axial, torsional, and bending strength showed only a modest reduction. Considering its other advantages, which include radiolucency and artifact-free imaging, the CF-PEEK locking plate therefore deserves further clinical investigation.