Improved reliability of mechanical behavior for a thermal tempered lithium disilicate glass-ceramic by regulating the cooling rate.

Abstract

Traditional thermal tempering was applied to lithium disilicate (LD) glass-ceramic specimens with bar-like and disc-like shapes. The tempering process was conducted by heating the specimens to a temperature below the dynamic softening point, and then rapid cooling in silicone oil with different temperatures ranging from room-temperature to 300 °C to regulate the cooling rate. Effect of the oil-temperature on mechanical behavior of the tempered glass-ceramic was investigated. For the tempering at the lower oil-temperature (e.g., at room-temperature), it was found that the LD glass-ceramic specimens with both the bar-like and disc-like shapes could be remarkably strengthen and toughen, however, obvious anisotropy in fracture toughness was displayed by the specimens with the bar-like shape. With increasing the oil-temperature up to 250 °C, the mechanical anisotropy of the bar-like specimens could be significantly alleviated without much loss of the strengthening effect. The results can provide references for improving reliability of mechanical behavior for the tempered LD glass-ceramic by regulating the cooling condition according to specimen geometry.