Abstract
Non-invasive estimation of cartilage material properties is useful for understanding cartilage health and creating subject-specific computational models. Bi-component T2 mapping measured using Multi-Component Driven Equilibrium Single Shot Observation of T<sub>1</sub> and T<sub>2</sub> (mcDESPOT) is sensitive for detecting cartilage degeneration within the human knee joint, but has not been correlated with cartilage composition and mechanical properties. Therefore, the purpose of this study was to investigate the relationship between bi-component T<sub>2</sub> parameters measured using mcDESPOT at 3.0 T and cartilage composition and mechanical properties. Ex-vivo patellar cartilage specimens harvested from five human cadaveric knees were imaged using mcDESPOT at 3.0 T. Cartilage samples were removed from the patellae, mechanically tested to determine linear modulus and dissipated energy, and chemically tested to determine proteoglycan and collagen content. Parameter maps of single-component T<sub>2</sub> relaxation time (T<sub>2</sub>), the T<sub>2</sub> relaxation times of the fast relaxing macromolecular bound water component (T<sub>2F</sub>) and slow relaxing bulk water component (T<sub>2S</sub>), and the fraction of the fast relaxing macromolecular bound water component (F<sub>F</sub>) were compared to mechanical and chemical measures using linear regression. F<sub>F</sub> was significantly (p < 0.05) correlated with energy dissipation and linear modulus. T<sub>2</sub> was significantly (p ≤ 0.05) correlated with elastic modulus at 1 Hz and energy dissipated at all frequencies. There were no other significant (p = 0.13-0.97) correlations between mcDESPOT parameters and mechanical properties. F<sub>F</sub> was significantly (p = 0.04) correlated with proteoglycan content. There were no other significant (p = 0.19-0.92) correlations between mcDESPOT parameters and proteoglycan or collagen content. This study suggests that F<sub>F</sub> measured using mcDESPOT at 3.0 T could be used to non-invasively estimate cartilage proteoglycan content, elastic modulus, and energy dissipation.
Medical subject headings
- Cartilage, Articular