Dispersion-Controlled Gold-Aluminum-Silicon Dioxide-Aluminum Nanopawn Structures for Visible to NIR Light Modulation.

Abstract

As an efficient patterning method for nanostructures, nanocolloidal lithography (NCL) presents a controllable and scalable means for achieving a uniform and good sidewall profile, and a high aspect ratio. While high selectivity between the etching mask and targeted materials is also essential for NCL-based precision nanophotonic structures, its realization in multi-material nanophotonic structures still remains a challenge due to the dielectric- or metallic-material-dependent etching selectivity. Here, dispersion-controlled Au-NCL is proposed, which enables high selectivity for Al and SiO₂ over a Au nanoparticle (Au-NP) mask. Utilizing the proposed process, wafer-scale, uniformly dispersed multi-material nanopawn structures (Au-NPs/Al-SiO₂ cylinders) on an Al ultrathin film are realized, obtaining excellent vertical sidewall (≈90°) and aspect ratio (>1). The high sidewall verticality and aspect ratio of the nanopawn structures support optical modes highly sensitive to the excitation direction of incident waves through the mixing of the interface-gap-assisted localized surface plasmons (GLSPs) formed in between the Au-NP and Al-disk interface, and plasmonic Fabry-Pérot (FP) modes formed in between the Al-disk and Al substrate; complementary spectral responses between reflected and scattered light are also demonstrated. As an application example, information encryption based on the triple-channel (i.e., reflection, scattering, and transmission) angle-dependent complementary-color responses is presented.