Efficacy of hydrated phospholipid polymer interfaces between all-polymer bearings for total hip arthroplasty.

Abstract

Measurements of wear resistance and metal ion release are important for designing bearing couples or interfaces in total hip arthroplasty (THA). In this study, we investigated wear resistance and metal ion release of surface-modified metal-free all-polymer hip bearings, such as poly(ether-ether-ketone), (PEEK) on cross-linked polyethylene (PEEK-on-CLPE), with a hydrated gel-like surface layer, to propose an improved alternative to the conventional materials used to design THA bearings. The PEEK surface resulted in less metal ion release than the cobalt-chromium-molybdenum (Co-Cr-Mo) alloy surface owing to the lack of metal. The PEEK-on-CLPE bearing (6.33 mg/10⁶  cycles) had lower wear (rate) than the bearing with Co-Cr-Mo alloy-on-CLPE (10.47 mg/10⁶  cycles) under controlled laboratory conditions; the wear performance of the all-polymer hip bearings was further improved with hemi- or both-surface modified with a hydrated poly(2-methacryloyloxyethyl phosphorylcholine) (PMPC) layer (3.74 and 3.06 mg/10⁶  cycles, respectively). The PMPC-grafted interface of PEEK-on-CLPE will be especially suitable for THA candidates. This study is of key importance for the design of lifelong THA and a better understanding of the limitations resulting from using PEEK. Further studies are necessary to evaluate the possibility of using this material in artificial hips.