Mechanical properties and in vitro cytocompatibility of dense and porous Ti-6Al-4V ELI manufactured by selective laser melting technology for biomedical applications.

Abstract

The Ti-6Al-4V alloy is the most common biomaterial used for bone replacements and reconstructions. Despite its advantages, the Ti-6Al-4V has a high stiffness that can cause stress-shielding. In this work, we demonstrated that the selective laser melting (SLM) technology could be used to fabricate porosity in Ti-6Al-4V extra low interstitial (ELI) to reduce its stiffness while improving cell adhesion and proliferation. With a porosity of 14.04%, the elastic modulus of the porous Ti-6Al-4V ELI was reduced to 80 GPa. The compressive stress and the 3-point-bending flexural tests revealed that the porous Ti-6Al-4V ELI possessed a brittle characteristic. The additional pores within the beams of the lattice structures of porous Ti-6Al-4V ELI increased its surface arithmetic average roughness, R_a = 3.94 μm. The in vitro cytocompatibility test showed that the SLM printing process and the post-processes did not cause any toxicity in the MC3T3-E1 cells. The in vitro cell proliferation test also showed that the porous Ti-6Al-4V ELI increased the proliferation rate of osteogenic induced MC3T3-E1 cells on Day 7. The findings from this study would provide engineers and researchers with both the mechanical information and biological understanding of SLM printed porous Ti-6Al-4V ELI, and SLM printed dense Ti-6Al-4V ELI towards biomedical applications.