Effect of Nanoscale Ce<sub>0.8</sub>Gd<sub>0.2</sub>O<sub>2-δ</sub> Infiltrant and Steam Content on Ni-(Y<sub>2</sub>O<sub>3</sub>)<sub>0.08</sub>(ZrO<sub>2</sub>)<sub>0.92</sub> Fuel Electrode Degradation during High-Temperature Electrolysis.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 34606281.
- Also identified by DOI 10.1021/acs.nanolett.1c02937.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
Studies of Ni-yttria-stabilized zirconia (YSZ) fuel electrode degradation mechanisms in solid oxide electrolysis cells (SOECs) are complicated by the different possible Ni-YSZ microstructures and compositions, and the variations in the H<sub>2</sub>/H<sub>2</sub>O ratio encountered in an electrolysis stack. Here we describe a life testing scheme aimed at providing survey results on degradation as a function of the H<sub>2</sub>O-H<sub>2</sub> composition, with life tests carried out at five different steam contents from 90% to 10%. A Ni-YSZ-supported symmetric cell geometry is employed both with and without infiltrated nanoscale gadolinia-doped ceria (GDC). Impedance spectroscopy is utilized to observe changes in electrochemical characteristics during the life test, and a transmission-line-based equivalent circuit is used to model the data. Post-test electrode microstructures were observed. The results suggest that the GDC infiltrant reduces the electrode polarization resistance and provides more stable electrode polarization over a range of conditions.