Sub-3-Nanometer Domain Spacings of Ultrahigh-χ Multiblock Copolymers with Pendant Ionic Groups.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 34617441.
- Also identified by DOI 10.1021/acsnano.1c06734.
- No licence information is recorded for this record.
- Because redistribution is not established, this page shows the abstract only. Follow the links below for the full text.
Abstract
We investigated the temperature-dependent phase behavior and interaction parameter of polyethylene-based multiblock copolymers with pendant ionic groups. These step-growth polymers contain short polyester blocks with a single Li<sup>+</sup>SO<sub>3</sub><sup>-</sup> group strictly alternating with polyethylene blocks of <i>x</i>-carbons (PES<i>x</i>Li, <i>x</i> = 12, 18, 23). At room temperature, these polymers exhibit layered morphologies with semicrystalline polyethylene blocks. Upon heating above the melting point (∼130 °C), PES18Li shows two order-to-order transitions involving <i>Ia</i>3̅<i>d</i> gyroid and hexagonal morphologies. For PES12Li, an order-to-disorder transition accompanies the melting of the polyethylene blocks. Notably, a Flory-Huggins interaction parameter was determined from the disordered morphologies of PES12Li using mean-field theory: χ(<i>T</i>) = 77.4/<i>T</i> + 2.95 (<i>T</i> in Kelvin) and χ(25 °C) ≈ 3.21. This ultrahigh χ indicates that the polar ionic and nonpolar polyethylene segments are highly incompatible and affords well-ordered morphologies even when the combined length of the alternating blocks is just 18-29 backbone atoms. This combination of ultrahigh χ and short multiblocks produces sub-3-nm domain spacings that facilitate the control of block copolymer self-assembly for various fields of study, including nanopatterning.