Tough and self-healing hydrogels based on transient crosslinking by nanoparticles.

Abstract

In this investigation, transient crosslinking was constructed to obtain a hydrogel with excellent mechanical and self-healing properties. Firstly, core-shell particles with hydrophilic amino groups were prepared by emulsion polymerization and subsequently dispersed into hydrophobic association polyacrylamide hydrogels. Transient crosslinking was constructed through hydrogen bonding between core-shell particles and polyacrylamide. As a result, the hydrogels exhibited a tensile strength of 1.4 MPa and self-healing efficiency of 98% at 24 h. Furthermore, reconstruction of the transient crosslinking was confirmed from rheological measurements. Therefore, the essential reinforcement principle based on transient crosslinking would open a novel strategy to obtain hydrogels with superior toughness and self-healing properties.