Preparation of Ca doped wrinkled porous silica (Ca-WPS) for the improvement of apatite formation and mechanical properties of dental resins.

Abstract

The purpose of this work was to fabricate and characterize Ca doped wrinkled porous silica (Ca-WPS), and evaluate their effect on the mineralization and mechanical properties of resin composites as functional fillers. Ca-WPS were prepared by sol-gel method and characterized by scanning electron microscopy, transmission electron microscopy and N₂ adsorption-desorption measurements. The mineralization properties of the prepared Ca-WPS particles and the resin composites with different amount of Ca-WPS were evaluated by simulated body fluid (SBF) immersion method. The mechanical properties (flexural strength, flexural modulus, compressive strength and microhardness) of the dental resins containing unimodal Ca-WPS fillers and bimodal Ca-WPS fillers with nonporous silica were evaluated by a universal testing machine. Results showed that after immersing in SBF for 5 d, apatite formed on the surface of Ca-WPS and composites containing Ca-WPS fillers, indicating the excellent mineralization property of the prepared Ca-WPS. The mechanical properties of the dental resins increase with the increase of the proportion of unimodal Ca-WPS fillers. The dental resins with bimodal Ca-WPS fillers showed better mechanical properties than the group with only nonporous fillers at the same filler loading (60 wt%). Among all the samples, the dental composites filled with bimodal fillers (mass ratio of Ca-WPS: nonporous silica = 10:50, total filler loading 60 wt%) exhibited the best mechanical performance. The flexural strength, flexural modulus, compressive strength and microhardness of these samples were 26.96%, 42.75%, 16.04% and 54.1% higher than the composites with solid silica particles alone, respectively. Thus, the prepared Ca-WPS could effectively improve the apatite formation and mechanical properties of resin composites.