Biodegradable Zn-Dy binary alloys with high strength, ductility, cytocompatibility, and antibacterial ability for bone-implant applications.

Abstract

The unique combination of biodegradability, biocompatibility, and functionality of zinc (Zn)-based alloys makes them highly desirable for a wide range of medical applications. However, a long-standing problem associated with this family of biodegradable alloys in the as-cast state is their limited mechanical strength and slow degradation rate. Here we report the development of Zn-xDy (x = 1, 3, and 5 wt.%) alloys with high strength, ductility, cytocompatibility, antibacterial ability, and appropriate degradation rate for biodegradable bone-implant applications. Our results indicate that the mechanical properties of Zn-xDy alloys were effectively improved with increasing Dy addition and hot-rolling due to the second-phase strengthening. The hot-rolled (HR) Zn-3Dy alloy showed the best combined mechanical performance with an ultimate tensile strength of 270.5 MPa, a yield strength of 214.8 MPa, an elongation of 55.1%, and Brinell hardness of 75.9 HB. The corrosion and degradation rates of HR Zn-xDy alloys in Hanks' solution gradually increased with increasing Dy addition due to the intensification of galvanic corrosion. The HR Zn-3Dy alloy showed high antibacterial ability against S. aureus and cytocompatibility toward MC3T3-E1 cells among all the HR alloys. Overall, the HR Zn-3Dy alloy can be considered a promising biodegradable material for bone implants. STATEMENT OF SIGNIFICANCE: This work reports on Zn-xDy (x = 1, 3, and 5%) alloys fabricated by Dy alloying followed by hot-rolling for biodegradable bone-implant applications. Our findings demonstrate that the hot-rolled (HR) Zn-3Dy alloy showed the best combined mechanical performance with an ultimate tensile strength of 270.5 MPa, a yield strength of 214.8 MPa, an elongation of 55.1%, and Brinell hardness of 75.9 HB. The corrosion and degradation rates of HR Zn-xDy alloys in Hanks' solution gradually increased with increasing Dy addition due to the intensification of galvanic corrosion. Furthermore, the HR Zn-3Dy alloy showed greater antibacterial ability against S. aureus and the best cytocompatibility toward MC3T3-E1 cells among all the HR alloys.