4D printing of MXene hydrogels for high-efficiency pseudocapacitive energy storage.
basic_science · Level V
Where this comes from
- Record sourced from PubMed, PMID 36371429.
- Also identified by DOI 10.1038/s41467-022-34583-0 and PMC identifier 9653467.
- Licence recorded as CC BY.
- The licence permits redistribution, so the abstract is shown in full and the full text is available from the publisher.
Abstract
2D material hydrogels have recently sparked tremendous interest owing to their potential in diverse applications. However, research on the emerging 2D MXene hydrogels is still in its infancy. Herein, we show a universal 4D printing technology for manufacturing MXene hydrogels with customizable geometries, which suits a family of MXenes such as Nb2CTx, Ti3C2Tx, and Mo2Ti2C3Tx. The obtained MXene hydrogels offer 3D porous architectures, large specific surface areas, high electrical conductivities, and satisfying mechanical properties. Consequently, ultrahigh capacitance (3.32 F cm-2 (10 mV s-1) and 233 F g-1 (10 V s-1)) and mass loading/thickness-independent rate capabilities are achieved. The further 4D-printed Ti3C2Tx hydrogel micro-supercapacitors showcase great low-temperature tolerance (down to -20 °C) and deliver high energy and power densities up to 93 μWh cm-2 and 7 mW cm-2, respectively, surpassing most state-of-the-art devices. This work brings new insights into MXene hydrogel manufacturing and expands the range of their potential applications.