Water dissociation at the water-rutile TiO₂(110) interface from ab initio-based deep neural network simulations.

Abstract

The interaction of water with TiO₂ surfaces is of crucial importance in various scientific fields and applications, from photocatalysis for hydrogen production and the photooxidation of organic pollutants to self-cleaning surfaces and bio-medical devices. In particular, the equilibrium fraction of water dissociation at the TiO₂-water interface has a critical role in the surface chemistry of TiO₂, but is difficult to determine both experimentally and computationally. Among TiO₂ surfaces, rutile TiO₂(110) is of special interest as the most abundant surface of TiO₂'s stable rutile phase. While surface-science studies have provided detailed information on the interaction of rutile TiO₂(110) with gas-phase water, much less is known about the TiO₂(110)-water interface, which is more relevant to many applications. In this work, we characterize the structure of the aqueous TiO₂(110) interface using nanosecond timescale molecular dynamics simulations with ab initio-based deep neural network potentials that accurately describe water/TiO₂(110) interactions over a wide range of water coverages. Simulations on TiO₂(110) slab models of increasing thickness provide insight into the dynamic equilibrium between molecular and dissociated adsorbed water at the interface and allow us to obtain a reliable estimate of the equilibrium fraction of water dissociation. We find a dissociation fraction of 22 ± 6% with an associated average hydroxyl lifetime of 7.6 ± 1.8 ns<i>.</i> These quantities are both much larger than corresponding estimates for the aqueous anatase TiO₂(101) interface, consistent with the higher water photooxidation activity that is observed for rutile relative to anatase.